Lightweight nickel clad aluminum corrision resistance high
thermostability
Nickel clad aluminum belongs to the combination of rare metals and
non-ferrous metals. The advantages of nickel and aluminum are
combined to form a lightweight, corrosion resistant and high
temperature resistant clad material. ZEGOTA uses innovative
technology, high-end equipment and high-quality raw materials to
develop and produce high-quality nickel clad aluminum with high
combination rate, ultra-thin and good surface quality.
Advantages:
1. Lightweight: Aluminum, as the base material, can greatly improve
the quality characteristics of materials and achieve superior
balance in strength and weight.
2. Corrosion resistance: Because copper is easily oxidized in humid
environment, the nickel clad aluminum composite developed by ZEGOTA
has the advantages of corrosion resistance and high temperature
resistance, which greatly improves the service life of copper.
3. High thermostability: The most prominent feature of nickel
material is high temperature resistance. It attaches nickel to the
surface of aluminum to obtain a kind of high temperature resistant
"aluminum material".
Parameters:
| Clad material | Nickel | Aluminum | Aluminum |
| Aluminum | Nickel | Nickel |
| Nickel | / | / |
| Thickness(mm) | 0.01-4.0 | 0.04-4.0 | 0.01-4.0 |
| Width(mm) | 5.0-1500 | 5.0-1500 | 5.0-1500 |
Tensile strength (Mpa) | 230-300 | 260-320 | 300-350 |
Yield strength (Mpa) | 180-240 | 200-260 | 260-300 |
| Elongation(%) | ≥40 | ≥37 | ≥15 |
Application:
1. Aerospace Industry: At the beginning of aircraft and rocket, the
problem of high temperature and body weight caused by friction on
the body surface had not been solved. However, after the birth of
nickel clad aluminum materials, the problem has been thoroughly
solved because of its high temperature resistance and lightweight
characteristics.
2. Automobile industry: In order to reduce the weight of
automobiles, most of the engine components are made of nickel clad
aluminum instead of steel.
3. Smelting industry: In steelmaking industry, there are many parts
which will work under high temperature, such as furnace
gallbladder, radiator, aluminum pot and other parts which contact
with molten steel.