Ultra Thin Titanium Clad Steel Clad Titanium With High Temperature
Resistance And High Strength
Description:
Titanium clad steel clad Titanium material is a combination of
nonferrous metal and steel products, with low magnetic
characteristics. ZEGOTA adopts innovative technology, high-end
equipment and high-quality raw materials to develop and produce
high-quality titanium clad steel materials with leading ultra-thin,
lightweight and high-temperature resistance.
Advantages:
1. High strength: steel has a good quality strength ratio. In the
strength application design, Titanium clad steel clad Titanium
materials make full use of the high strength performance of steel.
2. High temperature resistance: titanium has a melting point of
1660 ° c and a boiling point of 3287 ° c. As a composite material,
it can withstand extreme high temperature when surface contact.
3. Corrosion resistance: Titanium clad steel clad Titanium material
is an ideal material for ships and Marine engineering and is known
as "Marine metal". Due to the formation of stable oxide film on the
surface, Titanium clad steel clad Titanium material will not cause
environmental problems caused by metal ion leakage due to corrosion
or erosion.
Application:
1. Industrial field: the use of titanium high temperature
resistance and non-toxic characteristics, combined with steel with
high strength performance, in the power plant chimney use, to
achieve a lasting, environmentally friendly effect.
2. Marine engineering: Titanium clad steel clad Titanium has been
used in the field of Marine civil engineering. Titanium basically
will not be corrosed in seawater, and titanium metal ions will not
be dissolved.
3. Light industry: the ultra-thin composite of titanium steel can
be made into spectacle frames, earrings, bracelets, etc. The weight
is lower than platinum, so it is completely lightweight.
Parameter:
| Clad material | Titanium | Titanium |
| Steel | Steel |
| Titanium | / |
| Thickness(mm) | 0.01-4.0 | 0.01-4.0 |
| Width(mm) | 5.0-1500 | 5.0-1500 |
| Tensile strength(Mpa) | 600-850 | 900-1200 |
| Yield strength(Mpa) | 530-790 | 830-1100 |
| Elongation(%) | ≥40 | ≥10 |